W14HH rail fastening system
The W14HH fastening system is expertly engineered to accommodate heavy rail traffic, handling an impressive maximum permissible axle load of 350 kN , Esteemed and trusted across Europe, Asia, the Middle East, North America, and Latin America.
Products Parameters
Technical Specification of W14HH Fastening system
- Ideal for heavy haul operations, this system thrives with concrete sleepers on ballasted tracks
- Boasting an axle load capacity of up to 350kN
- Designed for remarkable speeds reaching up to 160km/h
- Ensuring high longitudinal rail resistance, with a minimum of 9kN
- Outstanding electrical resistance of at least 5 kΩ
- Features a clamping force for SKL14R, ideally set at 11.5 kN
- Offers versatile gauge adjustments within a range of ±10 mm
- Optionally, enhance durability with an anti-abrasion pad, protecting fasteners from wear
- For efficiency, all components are available for pre-assembly at the sleeper factory
The complete W14HH fastening system for each sleeper features a comprehensive array of components:
4 pcs of robust screw spike DHS35-161
4 pcs of durable flat washer UIs7
4 pcs of resilient rail clip SKL14R
4 pcs of guide plate Wfp14K700R
4 pcs of sturdy plastic dowel SDU25
2 pcs of efficient rail pad Zw141/175/7
The W14HH rail fastening system is meticulously crafted for heavy haul rail, supporting a substantial maximum axle load of 350 kN.
A comprehensive set includes 4 pcs rail clips SKL14R, 4 pcs sleeper screws DHS35 with flat washer UIs7, 4 pcs guide plates Wfp-12 700R, 4 pcs plastic dowels SDU25, 2 pcs rail pads Zw141/175/7.
Technical Parameters
| Part name |
Item |
Technical requirement |
Remark |
| SKL14R clip |
Type |
Dia.14mm |
Application for different rail types |
| Material |
60Si2Mn |
Chemical composition(%): C: 0.57, Mn: 0.75, Si: 1.73, Cr: 0.07P:≤0.015, S: ≤0.006 |
| Finish |
Plain oiled, painting, or upon request |
500 hours salt spry test |
| Hardness |
42-47HRC |
|
| Fatigue life |
When clip spring deflection is 9.1mm, swing is 1.42mm, fatigue life is up to 3 million cycles without breaking. |
|
| Standard refers to |
DIN17221, GB/T1222 |
|
| DHS35-161 screw spike |
Type |
M24x161mm |
|
| Grade |
Grade 5.6: 35# |
Tensile strength: ≥500Mpa Yield strength: ≥300Mpa Elongation: ≥20% Cold bending: 90 degree without crack |
| Finish |
Plain oiled, oxide black, zinc plated, hot dip galvanized, Dacromet, Sherardizing |
500 hours salt spry test |
| Standard refers to |
ISO898-1, UIC864-1, and NF F500-50 |
|
| Flat washer ULS7 |
Type |
Uls7 |
|
| Material |
Q235 |
|
| Finish |
Plain oiled, Oxide black, Zinc plated, Hot dip galvanized, Dacromet, Sherardizing |
500 hours salt spry test |
| Standard refers to |
EN10025, EN10139 |
|
| Plastic dowel SDU25 |
Type |
For different sizes of screw spike |
|
| Material |
Reinforced Nylon 6 (PA6) |
Density: 1.15g/cm3 Tensile strength: 66.3Mpa Elongation: 31.3% Melting point: 228ºC Insulation resistance: ≥2.8×1012Ω Hardness: ≥114HRR |
| Color |
Black |
|
| Guide plate Wfp14k 700R |
Type |
UIC54,115RE rail, and size as ordered |
|
| Material |
Reinforced Nylon 6 (PA6+30%GF) |
Density: 1.39g/cm3 Tensile strength: 165Mpa Elongation: 3.5% Melting point: 226ºC Insulation resistance: ≥1.9×1012Ω Glass fiber content: 30-35% Hardness: ≥114HRR |
| Color |
Black |
|
| Rail pad Zw-141-175-7 |
Type |
UIC54, 115RE rail, and size as ordered |
|
| Material |
TPE (Thermoplastic Elastomer ) |
Density: 1.09g/cm3 Tensile strength: 4.23Mpa Tensile Modulus: 2.97Mpa Melting point: 200-220ºC Shore hardness: ≥40D |
| Color |
Black |
Audited Supplier 