Introducing the RNY rail fastening system, your reliable partner in ensuring the ultimate stability and longevity of rail tracks. This exceptional system is tailored for the 115RE rail, predominantly used in the dynamic regions of South America and Latin America.
Each comprehensive set comprises 4 SL bolts, 4 RNY elastic plates, 4 square elastic plates, 4 cylindrical cushions, 4 NY nylon washers, 4 flat washers, 4 nuts, and 2 rail pad U-2, perfectly curated for optimal performance.
Products Parameters
The RNY spring blade rail fastening system is a cornerstone of railway projects in Mexico and North America. Designed specifically to fasten 115RE steel rail securely onto concrete sleepers, it ensures robust and long-lasting connections.
Compared with other fastening systems, the RNY offers a host of advantages. It stands out as a cost-effective solution due to its simplified installation and maintenance process. Moreover, the intelligent spring blade technology significantly reduces noise and vibration, making it indispensable for railway lines traversing residential areas.
Globally, railway infrastructures turn to the spring blade fastening mechanism for its unparalleled reliability. It's particularly favored in high-speed rail systems where impeccable stability and security are non-negotiable. Engineered to sustain its sturdiness over time, this mechanism ensures rails remain fixed, minimizing accident risks and elevating railway safety standards.
Technical Parameter
| Part name |
Item |
Technical requirement |
Remark |
| RNY elastic plate |
Type |
5mm Thickness |
Application for different rail types |
| Material |
60Si2Mn |
Chemical composition(%): C: 0.56-0.64, Mn: 0.60-0.90, Si: 1.60-2.00, Cr: ≤0.35, P: ≤0.03, S: ≤0.03 |
| Finish |
Plain oiled, red color painting, or upon request |
Offered as ordered |
| Hardness |
42-47HRC |
|
| Standard refers to |
DIN17221, GB/T1222 |
|
| Rail pad U-2 |
Type |
Suitable for UIC54, 115RE rails |
|
| Material |
TPE (Thermoplastic Elastomer ) |
Density: 1.09g/cm3 Tensile strength: 4.23Mpa Tensile Modulus: 2.97Mpa Melting point: 200-220ºC Shore hardness: ≥40D |
| Finish |
Natural |
|
| Nylon washer |
Type |
NY nylon washer |
|
| Material |
Reinforced Nylon 6 (PA6) |
Density: 1.15g/cm3 Tensile strength: 66.3Mpa Elongation: 31.3% Melting point: 228ºC Insulation resistance: ≥2.8×1012Ω Hardness: ≥114HRR |
| Finish |
Natural |
|
| SL Bolt |
Type |
7/8*186/201 |
|
| Material |
45# |
Chemical composition(%): C: 0.45, Mn: 0.65, Si: 0.25, P: 0.016, S: 0.001 |
| Finish |
Plain oiled, oxide black, zinc plated, hot dip galvanized |
|
| Grade |
8.8 |
Tensile strength: ≥800Mpa Yield strength: ≥640Mpa Elongation: ≥12% |
| Nut |
Type |
7/8 |
|
| Material |
45# |
Chemical composition(%): C: 0.45, Mn: 0.65, Si: 0.25, P: 0.016, S: 0.001 |
| Finish |
Plain oiled, oxide black, zinc plated, hot dip galvanized |
|
| Grade |
8 |
HV295-353 |
| Flat washer |
Type |
50*23*3 |
|
| Material |
Q235 |
Chemical composition(%): C: 0.12-0.20, Mn: 0.30-0.70, Si: ≤0.3, P: ≤0.045, S: ≤0.045 |
| Finish |
Plain oiled, oxide black, zinc plated, hot dip galvanized |
|
| Hardness |
HV200-300 |