The RNY rail fastening system: engineered for unparalleled rail stability and safety. This cutting-edge system is ideal for the 115RE rail and finds its primary application across South America and Latin America, ensuring robust rail connections.
Each comprehensive set consists of: 4 pcs SL bolts, 4 pcs RNY elastic plates, 4 pcs square elastic plates, 4 pcs cylindrical cushions, 4 pcs NY nylon washers, 4 pcs flat washers, 4 pcs nuts, and 2 pcs rail pad U-2, collectively offering unrivaled fastening precision.
Products Parameters
The RNY spring blade rail fastening system is prominently utilized in railway projects throughout Mexico and North America. This state-of-the-art system is designed specifically to secure the 115RE steel rail onto concrete sleepers, offering unmatched reliability.
When compared to other fastening systems, it stands out with numerous advantages. It is more cost-effective due to its simpler installation and maintenance processes. Furthermore, the innovative spring blade technology significantly reduces noise and vibration, making it indispensable for railway tracks intersecting residential zones.
Globally, railway networks frequently adopt the spring blade fastening system. It is particularly favored in countries with advanced high-speed rail systems, where maintaining stability and security is paramount. Designed for long-term endurance, the spring blade mechanism ensures that rails are firmly secured in place, minimizing accident risks and significantly boosting the overall safety and efficiency of the railway infrastructure.
Technical Parameter
| Part name |
Item |
Technical requirement |
Remark |
| RNY elastic plate |
Type |
5mm Thickness |
Application for different rail types |
| Material |
60Si2Mn |
Chemical composition(%): C: 0.56-0.64, Mn: 0.60-0.90, Si: 1.60-2.00, Cr: ≤0.35, P: ≤0.03, S: ≤0.03 |
| Finish |
Plain oiled, red color painting, or upon request |
Offered as ordered |
| Hardness |
42-47HRC |
|
| Standard refers to |
DIN17221, GB/T1222 |
|
| Rail pad U-2 |
Type |
Suitable for UIC54, 115RE rails |
|
| Material |
TPE (Thermoplastic Elastomer ) |
Density: 1.09g/cm3 Tensile strength: 4.23Mpa Tensile Modulus: 2.97Mpa Melting point: 200-220ºC Shore hardness: ≥40D |
| Finish |
Natural |
|
| Nylon washer |
Type |
NY nylon washer |
|
| Material |
Reinforced Nylon 6 (PA6) |
Density: 1.15g/cm3 Tensile strength: 66.3Mpa Elongation: 31.3% Melting point: 228ºC Insulation resistance: ≥2.8×1012Ω Hardness: ≥114HRR |
| Finish |
Natural |
|
| SL Bolt |
Type |
7/8*186/201 |
|
| Material |
45# |
Chemical composition(%): C: 0.45, Mn: 0.65, Si: 0.25, P: 0.016, S: 0.001 |
| Finish |
Plain oiled, oxide black, zinc plated, hot dip galvanized |
|
| Grade |
8.8 |
Tensile strength: ≥800Mpa Yield strength: ≥640Mpa Elongation: ≥12% |
| Nut |
Type |
7/8 |
|
| Material |
45# |
Chemical composition(%): C: 0.45, Mn: 0.65, Si: 0.25, P: 0.016, S: 0.001 |
| Finish |
Plain oiled, oxide black, zinc plated, hot dip galvanized |
|
| Grade |
8 |
HV295-353 |
| Flat washer |
Type |
50*23*3 |
|
| Material |
Q235 |
Chemical composition(%): C: 0.12-0.20, Mn: 0.30-0.70, Si: ≤0.3, P: ≤0.045, S: ≤0.045 |
| Finish |
Plain oiled, oxide black, zinc plated, hot dip galvanized |
|
| Hardness |
HV200-300 |