RNY Rail Fastening System This sophisticated system is perfectly tailored for 115RE rail applications, primarily serving the railway infrastructure needs of South America and Latin America.
Each comprehensive kit includes: 4 SL bolts, 4 RNY elastic plates, 4 square elastic plates, 4 cylindrical cushions, 4 NY nylon washers, 4 flat washers, 4 nuts, and 2 robust rail pads U-2, ensuring a secure and reliable rail connection.
Product Parameters
The RNY Spring Blade Rail Fastening System is extensively utilized in railway projects across Mexico and North America. It excels in securing 115RE steel rail onto concrete sleepers, offering unwavering reliability.
Compared to other rail fastening systems, our solution offers numerous advantages. It is cost-effective, owing to its streamlined installation and maintenance processes. The innovative spring blade technology effectively minimizes noise and vibration, making it ideal for railway lines traversing residential zones.
Globally, the spring blade fastening mechanism is a staple in railway systems. It is highly favored in regions with high-speed rail networks, where stability and safety are paramount. This mechanism is engineered for lasting durability, ensuring the rails remain securely fastened, thereby mitigating accident risks and boosting the overall safety of the railway system.
Technical Parameter
| Part name |
Item |
Technical requirement |
Remark |
| RNY elastic plate |
Type |
5mm Thickness |
Application for different rail types |
| Material |
60Si2Mn |
Chemical composition(%): C: 0.56-0.64, Mn: 0.60-0.90, Si: 1.60-2.00, Cr: ≤0.35, P: ≤0.03, S: ≤0.03 |
| Finish |
Plain oiled, red color painting, or upon request |
Offered as ordered |
| Hardness |
42-47HRC |
|
| Standard refers to |
DIN17221, GB/T1222 |
|
| Rail pad U-2 |
Type |
Suitable for UIC54, 115RE rails |
|
| Material |
TPE (Thermoplastic Elastomer ) |
Density: 1.09g/cm3 Tensile strength: 4.23Mpa Tensile Modulus: 2.97Mpa Melting point: 200-220ºC Shore hardness: ≥40D |
| Finish |
Natural |
|
| Nylon washer |
Type |
NY nylon washer |
|
| Material |
Reinforced Nylon 6 (PA6) |
Density: 1.15g/cm3 Tensile strength: 66.3Mpa Elongation: 31.3% Melting point: 228ºC Insulation resistance: ≥2.8×1012Ω Hardness: ≥114HRR |
| Finish |
Natural |
|
| SL Bolt |
Type |
7/8*186/201 |
|
| Material |
45# |
Chemical composition(%): C: 0.45, Mn: 0.65, Si: 0.25, P: 0.016, S: 0.001 |
| Finish |
Plain oiled, oxide black, zinc plated, hot dip galvanized |
|
| Grade |
8.8 |
Tensile strength: ≥800Mpa Yield strength: ≥640Mpa Elongation: ≥12% |
| Nut |
Type |
7/8 |
|
| Material |
45# |
Chemical composition(%): C: 0.45, Mn: 0.65, Si: 0.25, P: 0.016, S: 0.001 |
| Finish |
Plain oiled, oxide black, zinc plated, hot dip galvanized |
|
| Grade |
8 |
HV295-353 |
| Flat washer |
Type |
50*23*3 |
|
| Material |
Q235 |
Chemical composition(%): C: 0.12-0.20, Mn: 0.30-0.70, Si: ≤0.3, P: ≤0.045, S: ≤0.045 |
| Finish |
Plain oiled, oxide black, zinc plated, hot dip galvanized |
|
| Hardness |
HV200-300 |